Influence of intermetallic phase (TiFe) on the microstructural evolution and mechanical properties of as-cast and quenched Ti-Mo-Fe alloys.
Article in Scientific reports, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
This study presents the phase analysis, microstructural characteristics, and mechanical property evaluation of the as-cast and quenched Ti-15Mo-xFe alloys with high iron content ranging from 4 to 12 weight percent. All the four alloys were produced in a vacuum-arc melting furnace. Heat treatment in the form of solution treatment was performed in a muffle furnace at a temperature of 1100 °C, with 1-h holding time and the samples were rapidly quenched in ice-brine. X-ray diffractometer (XRD) was used to analyses the phases present in each alloy whereas the optical microscope (OM) was employed to track the microstructural evolution and percentage porosity. The mechanical properties of the alloys were evaluated using a tensile test and compression test method while the micro-Vickers hardness measurements were conducted to evaluate hardness of the alloys. The XRD patterns of as-cast showed peaks belonging to the β and α″ phases and intermetallic B2 TiFe phases. The as quenched XRD peaks illustrated β phase only and Fe·Ti·O