Physicomechanical, Wettability, Corrosion, Thermal, and Microstructural Morphology Characteristics of Carbonized and Uncarbonized Bagasse Ash Waste-Reinforced Al-0.45Mg-0.35Fe-0.25Si-Based Composites: Fabrications and Characterizations.

An effort was being made to incorporate waste bagasse ash (WBA) both in carbonized and uncarbonized form into the formulation of Al6063 matrix-based metal matrix composites (MMC's) by partially substituting ceramic particles for them. In the process of developing composites, comparative research on carbonized WBA and uncarbonized bagasse powder was carried out in the role of reinforcement. Microstructure investigations revealed that carbonized WBA particles were properly distributed throughout the aluminum-base metal matrix alloy. They also had the appropriate level of wettability. The reinforcement of carbonized WBA particles in AA6063-based matrix material had a maximum tensile strength of 110 MPa and a maximal hardness of 39 BHN when 3.75 wt % of the particles were used. The deterioration in tensile strength (6.25 wt % of WBA) and the appearance of porosity and blowholes can be enumerated by tensile fractography-based scanning electron microscopy (SEM) analysis. The reinforcement of carbonized WBA particles in AA6063-based matrix material was found to have a maximal percent elongation of 14.42% and the highest fracture toughness of 15 Joules when 1.25 wt % of the particles were employed. For AA6063/3.75 wt % carbonized WBA-based MMC's, the minimum percent porosity was determined to be 5.83, and the minimum thermal expansion was found to be 45 mm