ArticleDental materials : official publication of the Academy of Dental Materials2024
Post-failure analysis of model resin-composite restorations subjected to different chemomechanical challenges.
Article in Dental materials : official publication of the Academy of Dental Materials, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
Abstract
objectiveThe current study aimed to evaluate the effects of different combinations of chemical and mechanical challenges on the failure load, failure mode and composition of the resulting fracture surfaces of resin-composite restorations.
methodsThree resin composites were used to fill dentin disks (2 mm inner diameter, 5 mm outer diameter, and 2 mm thick) made from bovine incisor roots. The model restorations, half of which were preconditioned with a low-pH buffer (48 h under pH 4.5), were subjected to diametral compression with either a monotonically increasing load (fast fracture) or a cyclic load with a continuously increasing amplitude (accelerated fatigue). The load or number of cycles to failure was noted. SEM was performed on the fracture surfaces to determine the proportions of dentin, adhesive, and resin composite.
resultsBoth cyclic fatigue and acid preconditioning significantly reduced the failure load and increased the proportion of interfacial failure in almost all the cases, with cyclic fatigue having a more pronounced effect. Cyclic fatigue also increased the amount of adhesive/hybrid layer present on the fracture surfaces, but the effect of acid preconditioning on the composition of the fracture surfaces varied among the resin composites. SIGNIFICANCE: The adhesive or hybrid layer was found to be the least resistant against the chemomechanical challenges among the components forming the model restoration. Increasing such resistance of the tooth-restoration interface, or its ability to combat the bacterial actions that lead to secondary caries following interfacial debonding, can enhance the longevity of resin-composite restorations.