The Impact of Silver Diamine Fluoride Only or Simultaneously With Potassium Iodide Treatment on the Bond Durability of Resin Composite Material on Primary Teeth.
Article in Cureus, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
We aim to evaluate the bond strength between resin composite and primary demineralized dentin, pretreated with silver diamine fluoride (SDF) and simultaneous SDF with potassium iodide (KI) after thermal aging. In this in vitro study, human carious-free primary molars were randomly assigned into three groups and prepared by exposing the superficial dentin. The primary dentin of each molar was demineralized. The first group (the control) received saline treatment before bond application. SDF was pretreated for the second group, whereas SDF and KI were used for the third. After that, the pretreated dentin was immediately built with resin composite bonded with a universal adhesive and kept wet for 24 hours. Then, the pretreated molars were prepared into beam specimens for microtensile bond strength (µTBS), 16 for each group, and subjected to thermal aging. Lastly, they were tested using a universal testing machine, and the resulting data were analyzed using one-way analysis of variance (ANOVA) followed by Tukey's post hoc test. It was found that the SDF-KI group had a significant difference with both the control and SDF groups (p < 0.05), while the control and SDF groups showed no significant differences (p = 0.310). The SDF-KI group had the highest mean value of 11.73 ± 4.39 megapascal (MPa). In contrast, the control group had the lowest mean value of 9.31 ± 3.41 MPa. Post hoc pairwise comparison results showed that SDF-KI pretreatment had a significantly higher strength value than the control and SDF groups. Pretreatment of demineralized primary dentin with SDF-KI does not negatively affect the immediate loading of resin composite. However, under the limitation of this study, KI application after SDF pretreatment is recommended to enhance the bond's durability of resin composite to demineralized dentin.