Change in the Low-Cycle Performance on the 3D-Printed Materials ABS, ASA, HIPS, and PLA Exposed to Mineral Oil.
Article in Polymers, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. An erratum has been issued. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed, 3 citations in OpenAlex.
- Multi-objective optimization of surface finish and VOC emissions in FFF 3D printing using ANN-NSGA-II approach.Scientific reports · 2025Article
- Article
- Article
Corrections and comments
- Erratum issued
Authors and funding
5 authors at 2 institutions in 2 countries.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Three-dimensionally printed parts are increasingly used in industry for quick repairs. They are often operated in the presence of grease, oil, and others. This article describes the effect of engine mineral oil on the fatigue life of 3D-printed FDM plastic samples. For this reason, this article aimed to investigate the influence of oil on the fatigue life of materials made using this technology. Samples made of ABA, ASA, PLA, and HIPS materials were printed with 100% fill. Divided into groups, they were stored for 15, 30, and 60 days in an oil bath at a room temperature of 23 °C and an increased temperature of 70 °C. To compare the effect of storage in oil, static tests were performed to determine the tensile strength of the specimens and to determine the load levels for the cyclic tests. Cyclic tests were performed to determine the effect of oil and temperature on the fatigue life. Internal structure studies of the specimens were performed using computed microtomography to determine the changes in the porosity of the specimens under the influence of oil. In the case of ABS, the oil-bathed samples showed a clear increase in the fatigue life, especially at 23 °C. For the ASA specimens, an increase was also evident, especially for the lower stress value. For HIPS and PLA, no clear effect of the oil bath on the fatigue life value of the samples was determined. Porosity studies using computed microtomography showed a clear decrease in the porosity of the samples as a result of the oil bath for all of them.