Phase transformation behavior and mechanical properties of HyFlex EDM nickel-titanium endodontic rotary instrument: Evaluation at body temperature.
Article in Journal of dental sciences, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Article
- Changes in the Surface Area and Volume of Hyflex EDM Instruments after Multiple Uses.Acta stomatologica Croatica · 2025Article
- Phase Transformation and Mechanical Behaviour of Different Heat-Treated Nickel-Titanium Rotary Instruments.International dental journal · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Background/purpose: Temperature-dependent phase compositional changes influence the mechanical properties of heat-treated nickel-titanium (NiTi) rotary instruments. This study evaluated the phase composition, bending properties, and cyclic fatigue resistance of HyFlex EDM NiTi rotary instruments against differently heat-treated and non-heat-treated NiTi instruments at body temperature (BT). Materials and methods: HyFlex EDM OneFile (EDM) instruments, heat-treated HyFlex CM (CM) and Twisted File (TF) instruments, and non-heat-treated K3 instruments (size #25/.08) were subjected to differential scanning calorimetry, and the martensitic, R-phase, and reverse transformation starting and finishing temperatures were determined. A cantilever bending test and a cyclic fatigue test were conducted at BT (37 °C ± 1.0 °C), and the bending load and number of cycles to failure (NCF) were recorded. Statistical analysis was performed using Kruskal-Wallis and Mann-Whitney U tests (α = 0.05). Results: TF and K3 had reverse transformation finishing temperatures lower than BT, while those for EDM and CM were higher than BT. The bending loads at a 0.5 mm deflection were in the order of EDM < TF < CM < K3 ( Conclusion: The EDM instrument had a reverse transformation finishing temperature higher than BT indicating its martensite/R-phase composition at BT. The EDM instrument had superior flexibility and greater resistance to cyclic fatigue than the CM, TF, and K3 instruments at BT.