Property of Modified Bovine Bone Glue as an Environmental Additive in Water-Based Drilling Fluids.

At present, animal bone glue (BG) is being widely used in many fields, but there are no studies reported on oilfield chemistry. In this paper, an environmental water-based drilling fluids additive named bromoethane-modified bone glue (BG) was developed by using bovine bone glue and bromoethane as raw materials, anhydrous ethanol as solvent, sodium hydroxide as alkaline hydrolysis agent, and sodium carbonate as a system pH regulator. The inhibition, filtration performance, and temperature resistance of BG were evaluated. Performance study results show that the linear swelling rate of sodium bentonite (Na-MMT) was decreased from 50.2% (in tap water) to 38.2% (in 4 wt % BG solutions), and filtration loss was reduced from 30 mL (in tap water) to 12 mL (in 5 wt % BG). Hot-rolling experiments show that the BG solution still exhibits good performance even after 16 h × 130 °C. The reasons for BG to achieve excellent performance were analyzed through scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD), ζ potential, thermogravimetric analysis (TGA), and microstructure. The results of SEM and FT-IR show that BG can fully dissolve in water and adsorb on the surface of clay particles by relying on its own adsorption functional groups such as -OH and -COOH. When 4% BG was added, ζ potential analysis revealed that the clay particle size declined by 0.502 μm, which indicated that BG can inhibit clay hydration swelling dispersion.