The Initial Stage of Climatic Aging of Basalt-Reinforced and Glass-Reinforced Plastics in Extremely Cold Climates: Regularities.
Article in Polymers, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Article
- Effect of 2000-Hour Ultraviolet Irradiation on Surface Degradation of Glass and Basalt Fiber-Reinforced Laminates.Polymers · 2025Article
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
Detailed analyses of the reasons for changes in the mechanical parameters of fiberglass exposed to different climatic zones have been made available in the literature; however, such detailed studies of basalt plastic do not yet exist. It is possible to make reasonable conclusions on the climatic resistance of reinforced plastics by monitoring the deformation-strength characteristics in combination with fractographic and DMA analyses of the solar- and shadow-exposed parts of the plastics; additionally, one can conduct analyses of the IR spectrum and the moisture sorbtion kinetics. As a starting point for the climatic aging of polymer composite materials, it is necessary to accept the time of exposure in which the maximum values of the elastic strength properties of polymeric materials are achieved. Based on the results of the DMA analysis, it was found that, unlike basalt-reinforced plastics (where the material is post-cured exclusively at the initial stage of the exposure), in glass-reinforced plastic, a process of destruction occurs. The formation of internal stresses in the material and their growth were determined through observing the duration of climatic exposure. The formation of closed porosity, depending on the duration of exposure, can be assessed using the values of the increase in the average moisture content. A set of experimental studies has established that glass-reinforced plastics are subject to greater destruction under the influence of a very cold climate than the basalt-reinforced plastic.