Influence of Aging on the Flexural Strength of PLA and PLA-X 3D-Printed Materials.
Article in Micromachines, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 4 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
4 citing papers in PubMed.
- Artificial Muscles: Electrostatic Actuation and Design Tradeoffs.Biomimetics (Basel, Switzerland) · 2026Review
- Does Aging Affect PolyJet™ 3D-Printed Teeth for Endodontics? A Micro-CT Evaluation.Journal of functional biomaterials · 2026Article
- Evaluation of PLA and PETG as 3D-Printed Reference Materials for Compressive Strength Testing.Materials (Basel, Switzerland) · 2025Article
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The three-point bending test is a valuable method for evaluating the mechanical properties of 3D-printed biomaterials, which can be used in various applications. The use of 3D printing in specimen preparation enables precise control over material composition and microstructure, facilitating the investigation of different printing parameters and advanced materials. The traditional approach to analyzing the mechanical properties of a material using a three-point bending test has the disadvantage that it provides only global information about the material's behavior. This means that it does not provide detailed insight into the local strain distribution within the material. However, the 2D Digital Image Correlation (DIC) method offers additional insight, especially in terms of strain localization. DIC is an optical technique that measures full-field displacements and strains on the surface of a sample. PLA and enhanced PLA-X material were utilized to create three-point bending samples. The aim of this paper was to analyze and compare the influence of aging on the mechanical properties of PLA and enhanced PLA-X materials using three-point bending coupled with the DIC method. The results showed statistically significant differences between the PLA and PLA-X, for both the new and aged materials. The aged PLA samples had the highest average value of maximal force around 68 N, which was an increase of 8.8% compared to the new PLA samples. On the other hand, the aged PLA-X material had an increase of 7.7% in the average maximal force compared to the new PLA-X samples. When comparing the two materials, the PLA samples had higher maximal force values, 6.2% for the new samples, and 7.3% for the aged samples. The DIC results showed that both the new PLA and PLA-X samples endured higher strain values at Points 1 and 2 than the aged ones, except for the aged PLA-X sample at Point 2, where the new sample had higher strain values. However, for the first 5 min of the experiment, both materials exhibited identical behavior, after which point significant differences started to occur for both materials, as well as at Points 1 and 2. A more profound comprehension of the biomechanical characteristics of both PLA and PLA-X material is essential to enhance the knowledge for potential biomedical applications. The DIC method was found to be a powerful tool for analyzing the deformation and failure behavior of samples and for complementing the traditional approach to material testing.