Peculiar reaction of oxidized zirconium from a total knee arthroplasty prosthesis: A case report.
Article in Acta orthopaedica et traumatologica turcica, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Oxidized zirconium (OxiniumTM) prostheses, made up of a metallic alloy of zirconium with a ceramic surface formed by oxidizing the outer layer, were developed as an alternative bearing surface to reduce polyethylene wear and decrease failure of total knee arthroplasty (TKA). We report a unique catastrophic failure of an Oxinium TKA with consequent accelerated wear and severe metallosis. Intraoperatively, we observed extensive wear grooving of the femoral component with exposure of the underlying silver layers and the complete wear of polyethylene on the medial side. Metallic debris had a peculiar arthrogram appearance, noted within the cut surface of the femur and tibia, indicative of the osteolysis that occurred, leading up to the failure of the implants. The histopathologic examination revealed a collection of macrophages with foreign-body reactions and black-pigmented metal-induced wear particles. Oxinium has clear benefits regarding superior wear properties; however, surgeons need to be aware that there is a risk of exposure to the underlying layers that may precede accelerated wear, deformation, and metallosis. Uncovering the deeper layers could result in the appearance of an arthrogram on plain radiographs. Early identification of polyethylene wear and prompt revision is crucial to avoid the rapid progression of subsequent metallosis and catastrophic implant failure, specifically when using oxidized zirconium components for TKA. To the best of our knowledge, this is the first report presenting a detailed histologic analysis to provide insight into the mechanisms of the failed Oxinium components.
Indexed as
Identifiers
What OpenQuestion holds
Registered trials
Read under generation 80e0d062 · epoch 390. Bibliography from PubMed, PubMed Central and OpenAlex; grants from NIH RePORTER; trial links from ClinicalTrials.gov; estimates, votes and beliefs from the OpenQuestion graph.