Comparison of the Microstructural, Mechanical and Corrosion Resistance Properties of Ti6Al4V Samples Manufactured by LENS and Subjected to Various Heat Treatments.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 7 citations in OpenAlex.
- The Influence of Hot Isostatic Pressing on the Mechanical Properties of Ti-6Al-4V Samples Printed Using the LENS Method.Materials (Basel, Switzerland) · 2025Article
- The Chemistry-Process-Structure Relationships of a Functionally Graded Ti-6Al-4V/Ti-1B Alloy Processed with Laser-Engineered Net Shaping Creates Borlite.Materials (Basel, Switzerland) · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors at 2 institutions in 1 country.
Funding
Abstract
In this paper, the influences of two post-heat treatments on the structural, mechanical and corrosion resistance properties of additively manufactured Ti6Al4V alloys were discussed in detail. The materials were produced using the laser engineering net shaping (LENS) technique, and they were subjected to annealing without pressure and hot isostatic pressing (HIP) under a pressure of 300 MPa for 30 min at temperatures of 950 °C and 1050 °C. Annealing without pressure led to the formation of a thin plate structure, which was accompanied by decreasing mechanical properties and increasing elongation and corrosion resistance values. For the HIP process, the formation of a thick plate structure could be observed, resulting in the material exhibiting optimal mechanical properties and unusually high elongation. The best mechanical and corrosion resistance properties were obtained for the material subjected to HIP at 950 °C.