Performance of Fabrics with 3D-Printed Photosensitive Acrylic Resin on the Surface.

Additive manufacturing (AM), also known as three-dimensional printing (3DP), has been widely applied to various fields and industries, including automotive, healthcare, and rapid prototyping. This study evaluates the effects of 3DP on textile properties. The usability of a textile and its durability are determined by its strength, washability, colorfastness to light, and abrasion resistance, among other traits, which may be impacted by the application of 3DP on the fabric's surface. This study examines the application of photosensitive acrylic resin on two fabric substrates: 100% cotton and 100% polyester white woven fabrics made of yarns with staple fibers. A simple alphanumeric text was translated into braille and the braille dots were 3D printed onto both fabrics. The color of the printed photosensitive acrylic resin was black, and it was an equal mixture of VeroCyanV, VeroYellowV, and VeroMagentaV. The 3D-printed design was the same on both fabrics and was composed of braille dots with a domed top. Both of the 3DP fabrics passed the colorfastness to washing test with no transfer or color change, but 3D prints on both fabrics showed significant color change during the colorfastness to light test. The tensile strength tests indicated an overall reduction in strength and elongation when the fabrics had 3DP on their surface. An abrasion resistance test revealed that the resin had a stronger adhesion to the cotton than to the polyester, but both resins were removed from the fabric with the abrader. These findings suggest that while 3DP on textiles offers unique possibilities for customization and design, mechanical properties and color stability trade-offs need to be considered. Further evaluation of textiles and 3D prints of textiles and their performance in areas such as colorfastness and durability are warranted to harness the full potential of this technology in the fashion and textile industry.