Effect of lignocellulosic corn stalk on mechanical, physical, and thermal properties of injection moulded low density polyethylene composites: An approach towards a circular economy.

Escalating concern over global warming, which is mostly associated with deforestation, has led to the development of new classes of materials that can replace wood and better utilise natural resources. Presently, waste is a significant factor in recycling. In this regard, one of the leading contributors to waste is agricultural waste, which includes dried branches, leaves of trees, plants, and other organic materials. In the current study, waste from corn agriculture was utilised as a potential reinforcement for the fabrication of corn stalk-low density polyethylene (CS-LDPE) composites via an injection moulding technique at 170 °C. The different parameters were assessed to develop composites using CS, including physico-chemical, macromolecular, mineralogical, elemental, and morphological analysis. The amount of corn stalk (CS) was varied from 10 to 50 wt% with respect to the polymer. The mechanical, physical and thermal performance of the composites was examined. The density and water absorption of the composites were found to remain within the ranges of 1.00-1.11 g/cm