Axial Growth Characteristics of Optically Active InGaAs Nanowire Heterostructures for Integrated Nanophotonic Devices.

III-V semiconductor nanowire (NW) heterostructures with axial InGaAs active regions hold large potential for diverse on-chip device applications, including site-selectively integrated quantum light sources, NW lasers with high material gain, as well as resonant tunneling diodes and avalanche photodiodes. Despite various promising efforts toward high-quality single or multiple axial InGaAs heterostacks using noncatalytic growth mechanisms, the important roles of facet-dependent shape evolution, crystal defects, and the applicability to more universal growth schemes have remained elusive. Here, we report the growth of optically active InGaAs axial NW heterostructures via completely catalyst-free, selective-area molecular beam epitaxy directly on silicon (Si) using GaAs(Sb) NW arrays as tunable, high-uniformity growth templates and highlight fundamental relationships between structural, morphological, and optical properties of the InGaAs region. Structural, compositional, and 3D-tomographic characterizations affirm the desired directional growth along the NW axis with no radial growth observed. Clearly distinct luminescence from the InGaAs active region is demonstrated, where tunable array-geometry parameters and In content up to 20% are further investigated. Based on the underlying twin-induced growth mode, we further describe the facet-dependent shape and interface evolution of the InGaAs segment and its direct correlation with emission energy.