Flame-Retardant Behavior and Nanocrystal Synthesis through Formation of Multilayers of Poly(acrylic acid) and Zinc Phosphate on Cotton Fabric.
Article in ACS omega, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed, 7 citations in OpenAlex.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors at 1 institution in 1 country.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Cotton fabric with improved flame retardancy was prepared by introducing a zinc phosphate compound into cotton fabric using a layer-by-layer (LBL) deposition method with poly(acrylic acid) as a polymer electrolyte layer. In a vertical burning (VB) test, it was found that the flame retardancy improved as the number of depositions increased. As a result of thermogravimetric and inductively coupled plasma-atomic emission spectroscopy analyses, the residual amount increased to 20 wt % for the 20 deposited sample, and the weight ratio of Zn and P elements reached more than 40 wt %. As a result of SEM analysis, the cotton fibers not treated with LBL were destroyed after the VB test, but the shape of the fabric was maintained in the LBL-treated cotton fabrics. It was observed by TEM that numerous single crystals of about 10 nm formed on the surface of the sample subjected to the VB test. Through FT-IR and XPS analyses, it was confirmed that the zinc phosphate compound layer was formed by LBL deposition by the reaction between the phosphate anion and zinc cation. XRD analysis confirmed that the orthorhombic hopeite crystals produced by LBL deposition were transformed into zinc phosphate Zn