ArticlePolymers2024
Durability of Ultem 9085 in Marine Environments: A Consideration in Fused Filament Fabrication of Structural Components.
Article in Polymers, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
Abstract
The long-term durability of polymer components produced by additive manufacturing (AM) in marine conditions is poorly understood. Here, fused filament fabrication (FFF) of Ultem 9085 was conducted and accelerated aging was performed. Two printing orientations (-45/45° and 0/90°) and two sample types (ASTM D638 Type 1 and Type 4) were produced and subjected to accelerated aging in either seawater or air. Results from tensile tests showed that the elastic modulus, yield strength and ultimate tensile strength increased after seawater aging, whereas the elongation to failure decreased. Results of thermogravimetric analysis (TGA) and derivative-TGA curves indicated that hydrolysis occurred after seawater exposure to the polycarbonate (PC) component and changes in structure or hydrogen bonds formed in the polyetherimide (PEI) component. Differential scanning calorimetry showed that physical aging occurred after short exposure periods and low temperature. Longer exposures and higher temperatures resulted in increasing plasticization by water and scission of the PC molecules. Results from Raman suggest that hydrolysis of the PC occurred, with a reduction in free volume produced by physical aging or hydrogen bonding with water molecules. These results highlight that Ultem 9085 is susceptible to degradation in marine environments, and there are two primary mechanisms, including physical and chemical aging. Their specific contribution is highly sensitive to the aging temperature and require careful selection in accelerated aging evaluations.