Controlled Alignment of Carbon Black Nanoparticles in Electrospun Carbon Nanofibers for Flexible Films.

Carbon nanofiber (CNF) films or mats have great conductivity and thermal stability and are widely used in different technological processes. Among all the fabrication methods, electrospinning is a simple yet effective technique for preparing CNF mats, but the electrospun CNF mats are often brittle. Here, we report a feasible protocol by which to control the alignment of carbon black nanoparticles (CB NPs) within CNF to enhance the flexibility. The CB NPs (~45 nm) are treated with non-ionic surfactant Triton-X 100 (TX) prior to being blended with a solution containing poly(vinyl butyral) and polyacrylonitrile, followed by electrospinning and then carbonization. The optimized CB-TX@CNF mat has a boosted elongation from 2.25% of pure CNF to 2.49%. On the contrary, the untreated CB loaded in CNF displayed a lower elongation of 1.85% because of the aggregated CB spots created weak joints. The controlled and uniform dispersion of CB NPs helped to scatter the applied bending force in the softness test. This feasible protocol paves the way for using these facile surface-treated CB NPs as a commercial reinforcement for producing flexible CNF films.