Synthesis of a Calcium Silicate Cement Containing a Calcinated Strontium Silicate Phase.
Article in International journal of dentistry, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Effect of titanium dioxide nanotubes in Ca(OH)2-based intracanal medicaments on odontoblast-like cells.Brazilian oral research · 2026Article
- The Effect of Irrigation Solutions on the Setting Time, Solubility, and pH of Three Types of Premixed Bioceramic-Based Root Canal Sealers.International journal of dentistry · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Objectives: The positive effects of strontium on dental and skeletal remineralization have been confirmed in the literature. This study aimed to assess the properties of a calcium silicate cement (CSC) containing a sintered strontium silicate phase. Materials and Methods: The calcium silicate and strontium silicate phases were synthesized by the sol-gel technique. Strontium silicate powder in 0 (CSC), 10 (CSC/10Sr), 20 (CSC/20Sr), and 30 (CSC/30Sr) weight percentages was mixed with calcium silicate powder. Calcium chloride was used in the liquid phase. X-ray diffraction (XRD) of specimens was conducted before and after hydration. The setting time and compressive strength were assessed at 1 and 7 days after setting. The set discs of the aforementioned groups were immersed in the simulated body fluid (SBF) for 1 and 7 days. The ion release profile was evaluated by inductively coupled plasma-optical emission spectrometry (ICP-OES). Biomineralization on the specimen surface was evaluated by scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS). Data were analyzed by the Kolmogorov-Smirnov test, one-way and mixed ANOVA, Levene's test, and LSD post hoc test ( Results: Except for an increasement in the peak intensity of hydrated specimens, XRD revealed no other difference in the crystalline phases of hydrated and nonhydrated specimens. The compressive strength was not significantly different at 1 and 7 days in any group ( Conclusion: Incorporation of 10-30 wt% sintered strontium silicate phase as premixed in CSC can significantly decrease the setting time without compromising the compressive strength or biomineralization process of the cement.