New insight into biodegradable macropore filler on tuning mechanical properties and bone tissue ingrowth in sparingly dissolvable bioceramic scaffolds.

Structural parameters of the implants such as shape, size, and porosity of the pores have been extensively investigated to promote bone tissue repair, however, it is unknown how the pore interconnectivity affects the bone growth behaviors in the scaffolds. Herein we systematically evaluated the effect of biodegradable bioceramics as a secondary phase filler in the macroporous networks on the mechanical and osteogenic behaviors in sparingly dissolvable bioceramic scaffolds. The pure hardystonite (HT) scaffolds with ∼550 & 800 μm in pore sizes were prepared by digital light processing, and then the Sr-doped calcium silicate (SrCSi) bioceramic slurry without and with 30 % organic porogens were intruded into the HT scaffolds with 800 μm pore size and sintered at 1150 °C. It indicated that the organic porogens could endow spherical micropores in the SrCSi filler, and the invasion of the SrCSi component could not only significantly enhance the compressive strength and modulus of the HT-based scaffolds, but also induce osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs). The pure HT scaffolds showed extremely slow bio-dissolution in Tris buffer after immersion for 8 weeks (∼1 % mass decay); in contrast, the SrCSi filler would readily dissolve into the aqueous medium and produced a steady mass decay (>6 % mass loss).