The Impact of NaOH on the Micro-Mechanical Properties of the Interface Transition Zone in Low-Carbon Concrete.

To tackle carbon emissions from cement production and address the decline in concrete's mechanical properties due to the substitution of cement with solid waste (glass powder) and natural mineral admixture (zeolite powder) materials, we employed glass powder and zeolite powder to create composite cementitious materials. These materials underwent alkali activation treatment with a 4% NaOH dosage, replacing 50% of cement to produce low-carbon concrete. Nanoindentation tests and mercury intrusion porosimetry (MIP) were employed to uncover the micro-mechanical properties and influencing mechanisms of alkali-activated low-carbon concrete. The results indicate a notable enhancement in the indentation modulus (19.9%) and hardness (25.9%) of alkali-activated low-carbon concrete compared to non-activated concrete. Simultaneously, the interfacial transition zone thickness decreased by 10 µm. The addition of NaOH led to a reduced volume fraction of pores (diameter >100 nm) and an increased fraction of pores (diameter < 100 nm), thereby reducing porosity by 2.6%, optimizing the pore structure of low-carbon concrete. The indentation modulus, hardness and volume fraction of the hydrated phase derived from Gaussian fitting analysis of the nanoindentation statistics showed that NaOH significantly improved the modulus and hardness of the hydration products of low-carbon concrete. This activation resulted in decreased LDC-S-H gel (low-density hydrated calcium silicate Ca