Ultra-Smooth Polishing of Single-Crystal Silicon Carbide by Pulsed-Ion-Beam Sputtering of Quantum-Dot Sacrificial Layers.

Single-crystal silicon carbide has excellent electrical, mechanical, and chemical properties. However, due to its high hardness material properties, achieving high-precision manufacturing of single-crystal silicon carbide with an ultra-smooth surface is difficult. In this work, quantum dots were introduced as a sacrificial layer in polishing for pulsed-ion-beam sputtering of single-crystal SiC. The surface of single-crystal silicon carbide with a quantum-dot sacrificial layer was sputtered using a pulsed-ion beam and compared with the surface of single-crystal silicon carbide sputtered directly. The surface roughness evolution of single-crystal silicon carbide etched using a pulsed ion beam was studied, and the mechanism of sacrificial layer sputtering was analyzed theoretically. The results show that direct sputtering of single-crystal silicon carbide will deteriorate the surface quality. On the contrary, the surface roughness of single-crystal silicon carbide with a quantum-dot sacrificial layer added using pulsed-ion-beam sputtering was effectively suppressed, the surface shape accuracy of the Ø120 mm sample was converged to 7.63 nm RMS, and the roughness was reduced to 0.21 nm RMS. Therefore, the single-crystal silicon carbide with the quantum-dot sacrificial layer added via pulsed-ion-beam sputtering can effectively reduce the micro-morphology roughness phenomenon caused by ion-beam sputtering, and it is expected to realize the manufacture of a high-precision ultra-smooth surface of single-crystal silicon carbide.