ArticleBMC oral health2024
Flexural strength, flexural modulus and microhardness of milled vs. fused deposition modeling printed Zirconia; effect of conventional vs. speed sintering.
Article in BMC oral health, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 6 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
6 citing papers in PubMed, 17 citations in OpenAlex.
- Comparative Evaluation of Mechanical Properties Between CAD/CAM-Milled and 3D-Printed Dental Zirconia: A Systematic Review and Meta-Analysis.Materials (Basel, Switzerland) · 2025Review
- Evaluation of fracture resistance and surface characteristics in monolithic zirconia: a comparative analysis of 3D printing and milling techniques.BMC oral health · 2025Article
- The Effect of Acidic Immersion Media on the Flexural Properties of a High-Performance Fiber-Reinforced CAD/CAM Technopolymer.Polymers · 2025Article
- Review
- Bond Strength of Milled and Printed Zirconia to 10-Methacryloyloxydecyl Dihydrogen Phosphate (10-MDP) Resin Cement as a Function of Ceramic Conditioning, Disinfection and Ageing.Materials (Basel, Switzerland) · 2024Article
- Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors at 2 institutions in 1 country.
Funding
Abstract
backgroundVarious methods can be used for creating zirconia dental restorations, including 3-dimensional (3D) printing and computer-aided design/ computer-aided manufacturing (CAD/CAM) milling. The fused deposition modeling (FDM) printing method for zirconia presents numerous advantages, albeit research on the mechanical properties of these materials and resultant restorations remains scarce. Such developments are undeniably intriguing and warrant further investigation. The objective of the present study was to evaluate the impact of the sintering firing cycle (Conventional vs. Speed sintering) on the flexural strength, flexural modulus, and Vickers Microhardness of milled vs. FDM printed zirconia.
methodsA total of 60 bars (2 × 5 × 27 mm) were fabricated for flexural strength testing, along with 40 discs (12 × 1.5 mm) for Vickers microhardness testing. Half of the specimens underwent conventional sintering, while the other half underwent a speed sintering cycle. The flexural strength and modulus were determined by a three-point bending test in a universal testing machine. The microhardness of the specimens was evaluated using a Vickers microhardness tester. Statistical analysis was performed using a two-way ANOVA test with a post-hoc Tukey test (p < 0.05).
resultsCAD/CAM milled zirconia had significantly higher flexural strength and modulus than FDM-printed zirconia. The sintering process did not significantly affect the flexural strength or modulus of milled or FDM-printed zirconia. The milled speed sintering group had significantly higher values in the Vickers microhardness test compared to the other groups.
conclusionsThe mechanical properties of FDM-printed zirconia specimens were not found to be comparable to those of milled zirconia. Speed sintering cycle may produce milled zirconia restorations with similar flexural strength and modulus to conventional sintering, and even higher Vickers Microhardness values.