Antibiofilm activity of biosynthesized silver and copper nanoparticles using Streptomyces S29.

Microbial resistance and biofilm formation have been considered as the main problems associated with microbial resistance. Several antimicrobial agents cannot penetrate biofilm layers and cannot eradicate microbial infection. Therefore, the aim of this study is the biological synthesis of silver and copper nanoparticles to assess their activities on bacterial attachment and on the viability of dormant cells within the biofilm matrix. Ag-NPs and Cu-NPs were biosynthesized using Streptomyces isolate S29. The biologically synthesized Ag-NPs and Cu-NPs exhibited brown and blue colors and were detected by UV/Vis spectrophotometry at 476 and 594 nm, respectively. The Ag-NPs showed an average size of 10-20 nm as indicated by TEM, and 25-35 nm for Cu-NPs. Both Ag-NPs and Cu-NPs were monodispersed with a polydispersity index of 0.1-0.546 and zeta potential were - 29.7, and - 33.7 mv, respectively. The biologically synthesized Ag-NPs and Cu-NPs significantly eliminated bacterial attachment and decreased the viable cells in the biofilm matrix as detected by using crystal violet and tri-phenyl tetrazolium chloride assays. Furthermore, Ag-NPs and Cu-NPs significantly eradicated mature biofilms developed by various Gram-negative pathogens, including A. baumannii, K. pneumoniae and P. aeruginosa standard strains and clinical isolates. Data were also confirmed at the molecular level with prominent elimination of biofilm gene expression carO, bssS and pelA in A. baumannii, K. pneumoniae and P. aeruginosa, respectively compared to untreated cells under the same conditions. As indicated, Ag-NPs and Cu-NPs could be used as adjuvant therapy in eradication of antibiotic resistance and biofilm matrix associated with Gram-negative bacterial infection.