Porous carbons prepared from a novel hard wood composite waste for effective adsorption of Pb(ii) and Cd(ii) ions.

In our previous investigations, a hard wood composite (HWC) was formulated by adding rice straw, as a filler to the recycled polystyrene foam waste at mass ratio (50/50) at 170 °C and pressed under 40 kPa. Here, the disposed HWC product as a model scrap was applied for production of porous carbons enclosed with graphene sheets. To attain this approach, HWC was hydrothermally carbonized (S1) followed by either post-heat treatment (S2) or potassium hydroxide (KOH, S3) activation at 750 °C for 2 hours. The properties of prepared samples were evaluated using SEM, ATR-IR, and porosity measurements. The adsorption performance of the obtained porous carbons toward removal of lead (Pb(ii)) and cadmium (Cd(ii)) ions from aqueous solutions was investigated under different operating conditions like contact time, initial pH, initial metal ions concentration and adsorbent dose. Kinetic models such as pseudo-first order, pseudo-second order and intraparticle diffusion were used to analyze the adsorption data. Langmuir, Freundlich, Dubinin-Radushkevich and Redlich-Peterson isotherms were applied. Thermodynamics and regeneration studies were performed. The sample (S3) comprised a micro-mesoporous carbon structure encompassed by graphene sheets, with the largest total surface area (422 m