Effect of Surface Textures and Fabrication Methods on Shear Bond Strength Between Titanium Framework and Auto-Polymerizing Acrylic Repair Resin.
Article in Cureus, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed, 3 citations in OpenAlex.
- In vitro evaluation of bond strength between dental ceramics and titanium frameworks produced by additive and subtractive methods.BMC oral health · 2025Article
- Article
- The effect of thermocycling on fracture resistance of zirconia crowns cemented with polylysine modified resin cements (Comparative in vitro study).Journal of oral biology and craniofacial researchArticle
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
1 author at 1 institution in 1 country.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The aim of the study was to evaluate the effect of airborne particle abrasion (using different sizes of alumina particles) on the shear bond strength (SBS) between cast and milled titanium metal frameworks and auto-polymerizing acrylic repair resin. Forty flat cylindrical titanium disks were divided into two main divisions: cast and milled titanium. The two divisions were further subdivided into four groups based on metal surface treatment. Three particle sizes of aluminum oxide air abrasive powders (50µm, 110µm, and 250µm) were used for metal surface treatment by airborne particle abrasion. One group was the control group with no surface treatment. Auto-polymerizing acrylic repair resin was applied to all titanium disks. The specimens were subjected to SBS testing using a universal testing machine (Instron Corporation, Norwood, Massachusetts, United States). Surface evaluation was performed using a scanning electron microscope. One-way ANOVA was used for statistical analysis. The results showed a significant increase in SBS after airborne particle abrasion of both milled and cast titanium groups (p<0.001). The SBS was directly proportional to the size of the aluminum oxide particles. The milled titanium group showed higher SBS values than the cast group when the surface was not treated with alumina particles (p < 0.001) and when the surface was treated with the smaller particle sizes of 50 µm, whereas the cast group demonstrated higher SBS values than the milled group (p < 0.01) when the particle size was increased to 110 µm and 250 µm. It could be concluded that SBS between titanium metal frameworks and auto-polymerizing repair acrylic resin was directly related to the size of the alumina airborne particle abrasives. The fabrication method of the titanium framework also influenced the SBS as the untreated milled frameworks demonstrated favorable SBS values compared to the untreated cast frameworks.
Indexed as
Identifiers
What OpenQuestion holds
Registered trials
Read under generation 80e0d062 · epoch 390. Bibliography from PubMed, PubMed Central and OpenAlex; grants from NIH RePORTER; trial links from ClinicalTrials.gov; estimates, votes and beliefs from the OpenQuestion graph.