ArticlePolymers2023
Interfacial Bond Properties of Underwater Concrete Coated with Bisphenol A Epoxy Resins.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
This study investigated changes in the interfacial properties of epoxy-coated concrete exposed to various conditions, regarding the epoxy type, coating equipment, and exposure environment and period. The measured coating thickness and pull-off bond strength exhibited diverse trends, depending on the exposure period and conditions. In the real sea (RS) environment, the average bond strengths for bisphenol A (BPA) (E1), BPA with zinc powder (E2), and BPA with cresyl glycidyl ether (E3) were 1.26, 1.93, and 1.92 MPa, respectively. The coating method did not significantly affect the measured coating thickness and strength values. The conventional roller (D1) exhibited the highest thickness variation, with a value of 214.45 μm. The RS condition significantly increased the coating thickness (34% to 158%) compared to the tap water (TW) condition. The exposure conditions had little impact on bond strength except for E3, which showed an increased strength (2.71 MPa) over 7-91 days, especially under RS conditions, while E2 remained constant at approximately 1.82 MPa. This study offers insights into factors influencing marine concrete coating performance and discusses limitations and future work.