Effects of Electrical Parameters on Micro-Arc Oxidation Coatings on Pure Titanium.
Article in Micromachines, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 4 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
4 citing papers in PubMed.
- Construction and Properties of SPI/PLA-PCL Composite Coating on Pure Titanium Surface.Micromachines · 2026Article
- Impact of Various Sleeve Materials on Temperature Variations During Guided Endodontic Access Cavity Preparation Utilizing Finite-Element Analysis.Clinical and experimental dental research · 2026Article
- Microarc Oxidation Coatings Doped with a Low Proportion of Yttrium Enhance the Osseointegration of Titanium Implants through the BMP/Smad Pathway.ACS biomaterials science & engineering · 2025Article
- Effect of ultrasound on the physicochemical, mechanical and adhesive properties of micro-arc oxidized coatings on Ti13Nb13Zr bio-alloy.Scientific reports · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The micro-arc oxidation process was used to apply a ceramic oxide coating on a pure titanium substrate using calcium acetate and sodium dihydrogen phosphate as an electrolyte. The influence of the current frequency and duty ratio on the surface morphology, phase composition, wear behavior, and corrosion resistance were analyzed by employing a scanning electron microscope, X-ray diffractometer, ball-on-disk apparatus, and potentiodynamic polarization, respectively. Analyses of the surface and cross-sectional morphologies revealed that the MAO films prepared via a low current frequency (100 Hz) and a high duty ratio (60%) had a lower porosity and were more compact. The medium (500 Hz) and high (1000 Hz) frequencies at the higher duty ratios presented with better wear resistance. The highest film thickness (11.25 µm) was achieved at 100 Hz and a 20% duty ratio. A negligible current density was observed when the frequency was fixed at 500 Hz and 1000 Hz and the duty cycle was 20%.