Effect of bioactive glass-containing dentin adhesives on microshear bond strength of composite restorations.
Article in Dental research journal, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed, 3 citations in OpenAlex.
- Micro-Tensile Bond Strength of a Mesoporous Bioactive Glass-Containing Universal Adhesive: An In Vitro Study on the Effects of Artificial Aging.Materials (Basel, Switzerland) · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors at 4 institutions in 2 countries.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Background: In general, bioactive glasses (BAGs) can react with tissue minerals and promote remineralization. However, the application of BAG in bonding agents and its impact on bond strength remain uncertain due to insufficient information and limited research in this area. Materials and Methods: This study employed a randomized controlled design to assess the effects of composite-bonding agents with varying BAG contents on shear bond strength and fracture pattern in sound and demineralized teeth, with and without thermocycling. Thus, 80 healthy third molars were randomly divided into two groups: sound teeth and demineralized teeth. Five bonding agents were applied to the prepared dentin surfaces, including four experimental composite-bonding agents with varying BAG content (0, 0.2, 0.5, and 2 wt%) and the Adper Single Bond commercial bonding as control. The shear bond strength of all samples was measured using a universal tester. The type of failure of each specimen was determined using a stereomicroscope. Kruskal-Wallis nonparametric test was performed on the obtained shear bond strength data followed by Mann-Whitney Results: Demineralization significantly decreased shear bond strength in the teeth samples. Adper Single Bond exhibited the highest shear bond strength values. The addition of BAG did not have a significant influence on shear bond strength, regardless of demineralization or thermocycling condition. Adhesive failure was the predominant type of failure in all groups. Conclusion: The incorporation of BAG filler up to 2 wt% did not result in significant changes in shear bond strength. Experimental adhesive bonding agents with 2 wt% BAG content demonstrated shear bond strengths comparable to the commercial bonding agent in sound nontreated, sound thermocycled, demineralized nontreated, and demineralized thermocycled groups.