Development of Biodegradable Thermosetting Plastic Using Dialdehyde Pineapple Stem Starch.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed, 6 citations in OpenAlex.
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors at 1 institution in 1 country.
Funding
Abstract
Starch extracted from pineapple stem waste underwent an environmentally friendly modification process characterized by low-energy consumption. This process resulted in the creation of dialdehyde pineapple stem starch featuring varying aldehyde contents ranging from 10% to 90%. Leveraging these dialdehyde starches, thermosetting plastics were meticulously developed by incorporating glycerol as a plasticizer. Concurrently, unmodified pineapple stem starch was employed as a control to produce thermoplastic material under identical conditions. The objective of streamlining the processing steps was pursued by adopting a direct hot compression molding technique. This enabled the transformation of starch powders into plastic sheets without the need for water-based gelatinization. Consequently, the dialdehyde starch-based thermosetting plastics exhibited exceptional mechanical properties, boasting a modulus within the range of 1862 MPa to 2000 MPa and a strength of 15 MPa to 42 MPa. Notably, their stretchability remained relatively modest, spanning from 0.8% to 2.4%. Comparatively, these properties significantly outperformed the thermoplastic counterpart derived from unmodified starch. Tailoring the mechanical performance of the thermosetting plastics was achieved by manipulating the glycerol content, ranging from 30% to 50%. Phase morphologies of the thermoset starch unveiled a uniformly distributed microstructure without any observable starch particles. This stood in contrast to the heterogeneous structure exhibited by the thermoplastic derived from unmodified starch. X-ray diffraction patterns indicated the absence of a crystalline structure within the thermosets, likely attributed to the establishment of a crosslinked structure. The resultant network formation in the thermosets directly correlated with enhanced water resistance. Remarkably, the thermosetting starch originating from pineapple stem starch demonstrated continued biodegradability following a soil burial test, albeit at a notably slower rate when compared to its thermoplastic counterpart. These findings hold the potential to pave the way for the utilization of starch-based products, thereby replacing non-biodegradable petroleum-based materials and contributing to the creation of more enduring and sustainable commodities.