The Durable Chitosan Functionalization of Cellulosic Fabrics.

In this work, the durability of chitosan functionalization of cellulosic textile substrates, cotton and cotton/polyester blended fabrics, was studied. Chitosan is a naturally occurring biopolymer that can be produced inexpensively. It should be dissolved in an acidic solution to activate its antimicrobial and other properties, i.e., good biocompatibility, bioabsorbability, wound healing, hemostatic, anti-infective, antibacterial, non-toxic, and adsorptive properties. The application of chitosan to textile products has been researched to achieve antimicrobial properties, but the durability, after several maintenance cycles, has not. Chitosan functionalization was carried out using maleic acid (MA) and 1,2,3,4-butanetetracarboxylic acid (BTCA) as crosslinking and chitosan-activating agents and sodium hypophosphite monohydrate as a catalyst. To determine durability, the fabrics were subjected to 10 maintenance cycles according to ISO 6330:2012 using Reference detergent 3 and drying according to Procedure F. The properties were monitored after the 3rd and 10th cycles. The crosslinking ability of chitosan with cellulosic fabrics was monitored by Fourier infrared spectrometry using the ATR technique (FTIR-ATR). Changes in mechanical properties, whiteness and yellowing, and antimicrobial properties were determined using standard methods. Compared to maleic acid, BTCA proved to be a better crosslinking agent for chitosan.