Hydrogelation of Regenerated Silk Fibroin via Gamma Irradiation.

Gamma irradiation, which is one of the more conventional sterilization methods, was used to induce the hydrogelation of silk fibroin in this study. The physical and chemical characteristics of the irradiation-induced silk fibroin hydrogels were investigated. Silk fibroin solution with a concentration greater than 1 wt% formed hydrogel when irradiated by gamma rays at a dose of 25 or 50 kGy. The hydrogel induced by 50 kGy of radiation was more thermally stable at 80 °C than those induced by 25 kGy of radiation. When compared to the spontaneously formed hydrogels, the irradiated hydrogels contained a greater fraction of random coils and a lower fraction of β-sheets. This finding implies that gelation via gamma irradiation occurs via other processes, in addition to crystalline β-sheet formation, which is a well-established mechanism. Our observation suggests that crosslinking and chain scission via gamma irradiation could occur in parallel with the β-sheet formation. The irradiation-induced hydrogels were obtained when the solution concentration was adequate to support the radiation crosslinking of the silk fibroin chains. This work has, therefore, demonstrated that gamma irradiation can be employed as an alternative method to produce chemical-free, random coil-rich, and sterilized silk fibroin hydrogels for biomedical applications.