Comparative Study of Flax and Pineapple Leaf Fiber Reinforced Poly(butylene succinate): Effect of Fiber Content on Mechanical Properties.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 5 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
5 citing papers in PubMed, 12 citations in OpenAlex.
- Valorization of Pineapple Leaf Waste for Methylene Blue Adsorption: A Comparative Study of Natural and Modified Adsorbents.ACS omega · 2025Article
- Article
- Closing Editorial.Polymers · 2024Article
- Article
- Preparation and Spectroscopic, Thermal, and Mechanical Characterization of Biocomposites of Poly(butylene succinate) and Onion Peels or Durum Wheat Bran.Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors at 3 institutions in 4 countries.
Funding
Abstract
In this study, we compare the reinforcing efficiency of pineapple leaf fiber (PALF) and cultivated flax fiber in unidirectional poly(butylene succinate) composites. Flax, known for robust mechanical properties, is contrasted with PALF, a less studied but potentially sustainable alternative. Short fibers (6 mm) were incorporated at 10 and 20% wt. levels. After two-roll mill mixing, uniaxially aligned prepreg sheets were compression molded into composites. At 10 wt.%, PALF and flax exhibited virtually the same stress-strain curve. Interestingly, PALF excelled at 20 wt.%, defying its inherently lower tensile properties compared to flax. PALF/PBS reached 70.7 MPa flexural strength, 2.0 GPa flexural modulus, and 107.3 °C heat distortion temperature. Comparable values for flax/PBS were 57.8 MPa, 1.7 GPa, and 103.7 °C. X-ray pole figures indicated similar matrix orientations in both composites. An analysis of extracted fibers revealed differences in breakage behavior. This study highlights the potential of PALF as a sustainable reinforcement option. Encouraging the use of PALF in high-performance bio-composites aligns with environmental goals.