ArticleMaterials (Basel, Switzerland)2023
The Influence of the Thermal Treatment of Copper Slag on the Microstructure and Performance of Phosphate Cements.
Article in Materials (Basel, Switzerland), 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed, 7 citations in OpenAlex.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors at 2 institutions in 3 countries.
Funding
Abstract
In general, phosphate cements have a very rapid setting reaction at room temperature. The same holds for copper slag-based phosphate cements. This means that using them as a binder, for instance as mortar, is always possible on a small scale, but very difficult on a large scale. In this paper, the heat treatment of the copper slag was shown to be an effective way to increase the setting time and keep the mix workable for an adequate period. The main objective of this research was to examine the changes in the phase composition of quenched copper slag after exposure to 500 °C and to evaluate the impact of these changes on the reactivity of the material in an acidic environment, as well as on the mechanical properties, microstructure, and structure of the produced phosphate cement materials. Various experimental methods were utilized to characterize the raw materials and the obtained phosphate cementitious materials, including isothermal microcalorimetry (TAM Air), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), as well as the determination of the chemical composition using X-ray fluorescence (XRF) and the particle size distribution. Furthermore, compressive strength tests were conducted to gauge the mechanical resistance of the materials. The main findings of this work revealed that subjecting the copper slag to a thermal treatment of 500 °C induced a partial transformation in its structure. The high temperature caused the oxidation of some of the divalent iron oxide in the slag, leading to the formation of hematite. This treatment increased the setting time and reduced the reactivity of the copper slag with phosphoric acid, ultimately enabling the production of a dense phosphate-based cementitious material with outstanding mechanical properties. The compressive strength of the newly developed cement was recorded to be greater than 78.9 MPa after 7 days, and this strength continued to increase, reaching 82.5 MPa after 28 days.