Comparison of Thermal Deformation Behavior and Characteristics of Mg-Gd-Y-Zn Alloys with and without Bulk LPSO Phase.
Article in Materials (Basel, Switzerland), 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Effects of Bulk LPSO Phases on Mechanical Properties and Fracture Behavior of As-Extruded Mg-Gd-Y-Zn-Zr Alloys.Materials (Basel, Switzerland) · 2023Article
- The Development of a High-Strength Mg-10.3Gd-4.4Y-0.9Zn-0.7Mn Alloy Subjected to Large Differential-Thermal Extrusion and Isothermal Aging.Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
9 authors.
Funding
Abstract
Alloys Mg-8Gd-4Y-0.6Zn-0.5Zr (referred to as 0.6Zn) without the bulk long-period stacking ordered (LPSO) phase and Mg-8Gd-4Y-1.1Zn-0.5Zr (referred to as 1.1Zn) containing the bulk LPSO phase were prepared and a series of hot compression tests were conducted to examine and evaluate the influence of the bulk LPSO phase on the thermal deformation behavior and characteristics of the Mg-Gd-Y-Zn-Zr alloy. The bulk LPSO phase affects the dynamic recrystallization behavior, resulting in differences in flow stress between two alloys under different conditions. Specifically, in the temperature range of 380~460 °C, compression at lower strain rates is beneficial for the LPSO phase to promote dynamic recrystallization, while compression at a high strain rate inhibits the dynamic recrystallization due to the severe deformation of the bulk LPSO phase to release the stress concentration instead. The increase in temperature helps the LPSO promote dynamic recrystallization. As a result, the LPSO phase promotes dynamic recrystallization at all experimental strain rates at 500 °C. Furthermore, the thermal processing maps of the 0.6Zn and 1.1Zn alloys are established, and their optimal processing windows are located at 500 °C/0.001~0.01 s