Tunable Magnetic Domain Patterns in Thickness-Gradient Nickel Films on Flexible PDMS Substrates.

Flexible magnetoelectronic devices (based on magnetic films) have great application prospects in the fields of information storages, bionic robotics, and electronic skins. The intrinsic stress and external loading are very important to modulate the structures and properties of flexible magnetic films due to the magnetoelastic coupling effect. Here, we report on tunable magnetic domain patterns in thickness-gradient nickel (Ni) films deposited on flexible polydimethylsiloxane substrates. It is found that stripe magnetic domains spontaneously form in the Ni films and their sizes increase with the film thickness. The internal stress evolves from tensile to compressive states with decreasing film thickness, leading to the formation of cracks in thicker regions and wrinkles in thinner regions. Meanwhile, the orientations of stripe magnetic domains change from the gradient direction to the orthogonal direction. The structural features, evolution behaviors, and physical mechanisms of the cracks, wrinkles, and magnetic domains are analyzed based on the stress theory and magnetoelastic coupling. Periodic gradient Ni films with large-scale regulations of stripe magnetic domains are also realized by masking of copper grids. This study helps to better understand the magnetoelastic coupling effect in gradient flexible magnetic films and provides a technique to modulate anisotropic magnetic properties by designing specific film systems.