Quantifying the Release of Titanium From the Titanium Dioxide-Impregnated Composites Used in Orthodontic Bonding.

backgroundPrevious literature data has extensively assessed the biocompatibility of various orthodontic adhesives and their components, where the results of most of the studies showed cytotoxic effects of different degrees owing to the unbound molecules released structurally from the cured components.

aimThe present in-vitro study was aimed to assess the release of titanium dioxide nanoparticles in the artificial saliva from the orthodontic composites impregnated with titanium dioxide nanoparticles of 5% w/w (weight/weight) and 1% w/w used for metal brackets bonding.

methodsThe study assessed 160 teeth extracted freshly during orthodontic treatment and divided into two groups of 80 samples, each that bonded to orthodontic brackets having 5% w/w and 1% w/w composites with titanium dioxide nanoparticles kept in the artificial saliva. Quantification was done for 5% w/w and 1% w/w composites having titanium nanoparticles with inductively coupled plasma mass spectroscopy at 24 hours, two, four, and six months.

resultsIt was seen that in teeth with 1% titanium dioxide, the greatest titanium release was seen at two months, with non-significant release after two months. In teeth with 5% w/w titanium dioxide nanoparticles showed significant titanium release all the time. A significantly greater titanium dioxide release on increasing concentration from 1% to 5% was seen for the 5% w/w group at all the assessment times.

conclusionThe present study concludes that a higher release of titanium is seen in 5% w/w composite containing titanium dioxide nanoparticles, and the concentrations of 1% and 5% can be safely used and are considered to be within permissible limits.