ArticlePolymers2023
Eco-Friendly Blends of Recycled PET Copolymers with PLLA and Their Composites with Chopped Flax Fibres.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed, 5 citations in OpenAlex.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors at 2 institutions in 2 countries.
Funding
Abstract
The structure and properties of blends of a novel polyethylene terephthalate copolymer (COPET) obtained by chemical recycling of commercial PET with high-molar-mass poly-L-lactide (PLLA) are investigated and compared to corresponding composites with chopped flax fibres. The focus is on the morphology at nano- and micro-scales, on the thermal characteristics and on the mechanical behaviour. The blends are immiscible, as evidenced by virtually unchanged glass transition temperatures of the blend components compared to the neat polymers (49 °C for COPET and 63 °C for PLLA by DSC). At low PLLA content, the blends display a sea-island morphology with sub-micron to micron droplet sizes. As the composition approaches 50/50, the morphology transitions to a coarser co-continuous elongated structure. The blends and composites show strongly improved stiffness compared to COPET above its glass transition temperature, e.g., from melt behaviour at 60 °C for COPET alone to almost 600 MPa for the 50/50 blend and 500 MPa for the 20% flax composite of the 80/20 COPET/PLLA blend. The flax fibres increase the crystallisation rate of PLLA in blends with dispersed PLLA morphology. The evidence of cavitation on the fracture surfaces of blends shows that despite the immiscibility of the components, the interfacial adhesion between the phases is excellent. This is attributed to the presence of aliphatic ester spacers in COPET. The tensile strength of the 80/20 blend is around 50 MPa with a Young's modulus of 2250 MPa. The corresponding 20% flax composite has similar tensile strength but a high Young's modulus equal to 6400 MPa, which results from the individual dispersion and strong adhesion of the flax fibres and leads close to the maximum possible reinforcement of the composite, as demonstrated by tensile tests and nano-indentation. The Ashby approach to eco-selection relying on the embodied energy (EE) further clarifies the eco-friendliness of the blends and their composites, which are even better positioned than PLLA in a stiffness versus EE chart.