Improving Mechanical and Barrier Properties of Antibacterial Poly(Phenylene Sulfide) Nanocomposites Reinforced with Nano Zinc Oxide-Decorated Graphene.

Nano zinc oxide-decorated graphene (G-ZnO) was blended with polyphenylene sulfide (PPS) to improve its tensile, thermal, crystalline, and barrier properties. The properties of neat PPS and PPS/G-ZnO nanocomposites were characterized and compared using various tests, including tensile tests, scanning electron microscopy, X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, evaluation of Escherichia coli inhibition, and barrier performance. The results demonstrated that G-ZnO played a crucial role in heterogeneous nucleation and reinforcement. When the concentration of G-ZnO was 0.3%, the tensile strength, elongation at break, thermostability, crystallinity, and water vapor permeability coefficients (WVPC) approached their maximum values, and the microscopic morphology changed from the original brittle fracture to a relatively tough fracture. In addition, when G-ZnO was added to PPS at a ratio of 0.3%, the tensile strength, elongation at break, and WVPC of PPS were increased by 129%, 150%, and 283%, respectively, compared to pure PPS. G-ZnO endowed the nanocomposites with antibacterial properties. The improvement in barrier performance can be attributed to three reasons: (1) the presence of G-ZnO extended the penetration path of molecules; (2) the coordination and hydrogen bonds between PPS polymer matrix and G-ZnO nanofiller narrowed the H