Influence of Aging Treatment Regimes on Microstructure and Mechanical Properties of Selective Laser Melted 17-4 PH Steel.
Article in Micromachines, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Additive Manufacturing of Metals Using the MEX Method: Process Characteristics and Performance Properties-A Review.Materials (Basel, Switzerland) · 2025Review
- Editorial for the Special Issue on Laser Additive Manufacturing: Design, Materials, Processes, and Applications, 2nd Edition.Micromachines · 2024Article
- Microstructure, Tensile Properties, and Fracture Toughness of an In Situ Rolling Hybrid with Wire Arc Additive Manufacturing AerMet100 Steel.Micromachines · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
10 authors.
Funding
Abstract
Aging is indispensable for balancing the strength and ductility of selective laser melted (SLM) precipitation hardening steels. This work investigated the influence of aging temperature and time on the microstructure and mechanical properties of SLM 17-4 PH steel. The 17-4 PH steel was fabricated by SLM under a protective argon atmosphere (99.99 vol.%), then the microstructure and phase composition after different aging treatments were characterized via different advanced material characterization techniques, and the mechanical properties were systematically compared. Coarse martensite laths were observed in the aged samples compared with the as-built ones, regardless of the aging time and temperature. Increasing the aging temperature resulted in a larger grain size of the martensite lath and precipitation. The aging treatment induced the formation of the austenite phase with a face-centered cubic (FCC) structure. With prolonged aging treatment, the volume fraction of the austenite phase increased, which agreed with the EBSD phase mappings. The ultimate tensile strength (UTS) and yield strength gradually increased with increasing aging times at 482 °C. The UTS reached its peak value after aging for 3 h at 482 °C, which was similar to the trend of microhardness (i.e., UTS = 1353.4 MPa). However, the ductility of the SLM 17-4 PH steel decreased rapidly after aging treatment. This work reveals the influence of heat treatment on SLM 17-4 steel and proposes an optimal heat-treatment regime for the SLM high-performance steels.