Impact of Cryogenic Treatment Process on the Performance of 51CrV4 Steel.
Article in Materials (Basel, Switzerland), 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Impact of Deep Cryogenic Treatment on X210CrW12 Steel's Wear Behavior and Microstructural Characteristics.Materials (Basel, Switzerland) · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The working load on automotive components is continuously rising, and the mechanical performance requirements for component materials are rising along with the growth trend toward light weight and high dependability in automobiles. In this study, the response characteristics of 51CrV4 spring steel were taken to be its hardness, wear resistance, tensile strength, and impact toughness. Prior to tempering, cryogenic treatment was introduced. Through the Taguchi method and gray relational analysis, the ideal process parameters were discovered. The ideal process variables were the following: a cooling rate of 1 °C/min, a cryogenic temperature of -196 °C, a holding time of 24 h, and a cycle number of three. An analysis of variance revealed that the holding time had the greatest effect on the material properties, with an effect of 49.01%. The yield limit of 51CrV4 was increased by 14.95% and the tensile strength was increased by 15.39% with this group of processes, and the wear mass loss was reduced by 43.32%. The mechanical qualities had a thorough upgrade. Microscopic analysis revealed that cryogenic treatment resulted in refinement of the martensite structure and significant differences in orientation. Additionally, bainite precipitation occurred, exhibiting a fine needle-like distribution, which positively influenced impact toughness. Analysis of the impact fracture surface showed that cryogenic treatment led to an increase in dimple diameter and depth. Further analysis of the elements revealed that calcium (Ca) weakened the negative effect of sulfur (S) on 51CrV4 spring steel. The overall improvement in material properties provides guidance for practical production applications.