Flexible and Scalable Dry Conductive Elastomeric Nanocomposites for Surface Stimulation Applications.

objectiveThe study describes the development and testing of a dry surface stimulation flexible electrode (herein referred to as Flexatrode), a low-cost, flexible, and scalable elastomeric nanocomposite using carbon black (CB) and polydimethylsiloxane (PDMS).

methodsFlexatrodes composed of CB and PDMS were developed and tested for mechanical and functional stability up to 7 days. Uniform CB distribution was achieved by optimizing the dispersion process using toluene and methyl-terminated PDMS. Electromechanical testing in the through thickness directions over a long-term duration demonstrated stability of Flexatrode. Thermal stability of Flexatrode for up to a week was tested and validated, thus mitigating concerns of heat generation and deleterious skin reactions such as vasodilation or erythema.

results25 wt.% CB was determined to be the optimal concentration. Electrical and thermal stability were demonstrated in the through thickness direction.

conclusionFlexatrode provides stable electrical properties combined with high flexibility and elasticity. Electrotherapy treated chronic wounds were 81.9% smaller than baseline at day 10. Wounds that received an inactive device (device without any electrical stimulation) were 58.1% smaller than baseline and wounds that received standard of care treatment were 62.2% smaller than baseline. SIGNIFICANCE: The increasing need for wearable bioelectronics requiring long-term monitoring/treatment has highlighted the limitations of sustained use of gel-based electrodes. These can include skin irritation, bacterial overgrowth at the electrode site, gel dehydration over time, and signal degradation due to eccrine sweat formation. Flexatrode provides stable performance in a nanocomposite with scalable fabrication, thus providing a promising platform technology for wearable bioelectronics.