Electrospun cellulose acetate/activated carbon composite modified by EDTA (rC/AC-EDTA) for efficient methylene blue dye removal.

The present study fabricated regenerated cellulose nanofiber incorporated with activated carbon and functionalized rC/AC3.7 with EDTA reagent for methylene blue (MB) dye removal. The rC/AC3.7 was fabricated by electrospinning cellulose acetate (CA) with activated carbon (AC) solution followed by deacetylation. FT-IR spectroscopy was applied to prove the chemical structures. In contrast, BET, SEM, TGA and DSC analyses were applied to study the fiber diameter and structure morphology, the thermal properties and the surface properties of rC/AC3.7-EDTA. The CA was successfully deacetylated to give regenerated cellulose nanofiber/activated carbon, and then ethylenediaminetetraacetic acid dianhydride was used to functionalize the fabricated nanofiber composite. The rC/AC3.7-EDTA, rC/AC5.5-EDTA and rC/AC6.7-EDTA were tested for adsorption of MB dye with maximum removal percentages reaching 97.48, 90.44 and 94.17%, respectively. The best circumstances for batch absorption experiments of MB dye on rC/AC3.7-EDTA were pH 7, an adsorbent dose of 2 g/L, and a starting MB dye concentration of 20 mg/L for 180 min of contact time, with a maximum removal percentage of 99.14%. The best-fit isotherm models are Temkin and Hasely. The outcome of isotherm models illustrates the applicability of the Langmuir isotherm model (LIM). The maximal monolayer capacity Q