Effects of organoclay on colorless and transparent polyimide nanocomposites: thermomechanical properties, morphology, and optical transparency.

Although aromatic polyimide (PI) exhibits excellent mechanical performance and thermal stability, its dark color limits applicability in optical displays. Therefore, it is desirable to manufacture colorless, transparent PI (CPI) nanocomposite films that retain excellent physical properties. In this study, a solution intercalation method was used to disperse organoclay (Cloisite 25A; CS25A) in poly(amic acid), which was prepared using 4,4'-oxydiphthalic dianhydride and 3,4'-oxydianiline as monomers. This dispersion was then subjected to thermal imidization to synthesize CPI hybrid films. The influence of the CS25A content (0-1.00 wt%) on the thermomechanical properties, optical transmittance, and morphology of the prepared films was investigated. The hybrid film with a CS25A content of 0.50 wt% exhibited the best thermomechanical properties. However, upon further increasing the organoclay content to 1.00 wt%, the physical properties deteriorated. At 0.50 wt% CS25A, some agglomeration occurred but most of the clay was well dispersed as nano-sized particles, as revealed by transmission electron microscopy. In contrast, when the CS25A content exceeded a critical content, most of the clay was agglomerated and the physical properties were reduced. All the obtained CPI hybrid films were colorless and transparent, regardless of the organoclay content.