The Synergistic Effects of Aminosilane Coupling Agent on the Adhesion Performance of Silane Primer for Silicone Resin Thermal Protection Coating.

As a bridge between the coating and the substrate, the primer has a direct impact on the adhesion performance of silicone resin thermal protection coating. In this paper, the synergistic effects of an aminosilane coupling agent on the adhesion performance of silane primer were investigated. The results show that silane primer containing N-aminoethyl-3-aminopropylmethyl-dimethoxysilane (HD-103) formed a continuous and uniform film on the surface of the substrate. Two amino groups of HD-103 were conducive to moderate and uniform hydrolysis of the silane primer system, and the introduction of dimethoxy groups was more conducive to the improvement of interfacial layer density and the formation of the planar surface structure, thus enhancing the bond strength at the interface. When the content was 13 wt%, it exhibited excellent synergistic effects on adhesive properties, and the adhesive strength reached 1.53 MPa. The possible morphology and composition of the silane primer layer were investigated by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). A thermogravimetric infrared spectrometer (TGA-IR) was used to analyze the thermal decomposition of the silane primer layer. The results showed that the alkoxy groups in the silane primer were first hydrolyzed to form Si-OH, and then the dehydration and condensation reactions between Si-OH and the substrate formed a firm network structure.