Tailoring Triple Filler Systems for Improved Magneto-Mechanical Performance in Silicone Rubber Composites.

The demand for multi-functional elastomers is increasing, as they offer a range of desirable properties such as reinforcement, mechanical stretchability, magnetic sensitivity, strain sensing, and energy harvesting capabilities. The excellent durability of these composites is the key factor behind their promising multi-functionality. In this study, various composites based on multi-wall carbon nanotubes (MWCNT), clay minerals (MT-Clay), electrolyte iron particles (EIP), and their hybrids were used to fabricate these devices using silicone rubber as the elastomeric matrix. The mechanical performance of these composites was evaluated, with their compressive moduli, which was found to be 1.73 MPa for the control sample, 3.9 MPa for MWCNT composites at 3 per hundred parts of rubber (phr), 2.2 MPa for MT-Clay composites (8 phr), 3.2 MPa for EIP composites (80 phr), and 4.1 MPa for hybrid composites (80 phr). After evaluating the mechanical performance, the composites were assessed for industrial use based on their improved properties. The deviation from their experimental performance was studied using various theoretical models such as the Guth-Gold Smallwood model and the Halpin-Tsai model. Finally, a piezo-electric energy harvesting device was fabricated using the aforementioned composites, and their output voltages were measured. The MWCNT composites showed the highest output voltage of approximately 2 milli-volt (mV), indicating their potential for this application. Lastly, magnetic sensitivity and stress relaxation tests were performed on the hybrid and EIP composites, with the hybrid composite demonstrating better magnetic sensitivity and stress relaxation. Overall, this study provides guidance on achieving promising mechanical properties in such materials and their suitability for various applications, such as energy harvesting and magnetic sensitivity.