Properties and Structure of Thermoplastic Polyvinyl Alcohol/Polyamide Sea-Island Fibers.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed, 17 citations in OpenAlex.
- Annealed Polyvinyl Alcohol Hydrogels for Cartilage Replacement: Effects of Synthesis Parameters on Mechanical Properties.Gels (Basel, Switzerland) · 2025Article
- Article
- Fabrication of PVA Coatings Applied to Electrospun PLGA Scaffolds to Prevent Postoperative Adhesions.Journal of functional biomaterials · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors at 1 institution in 1 country.
Funding
Abstract
Ultra-fine fibers derived from sea-island fibers have attracted great attention due to their excellent overall performance. However, green and efficient splitting of sea-island fibers is still a challenging task. In this work, thermoplastic polyvinyl alcohol (TPVA) was prepared by the physical blending of plasticizer. The modified TPVA showed a high decomposition temperature (285 °C) and a wide thermoplastic processing window. This made TPVA match well with polyamide 6 (PA6) to form conjugated melts at 250 °C. Corresponding PVA/PA6 sea-island fibers were first reported to realize water-splitting instead of alkali-extraction of "sea" polymers. The effects of sea/island mass ratios and different spinning speeds on the properties of PVA/PA6 sea-island pre-oriented yarn (POY) were investigated. A higher spinning speed enhanced the orientation-induced crystalline behavior of fiber, therefore increasing the tensile strength of fibers. As the increase of spinning speed from 1000 to 1500 m/min, the crystalline degree of corresponding POYs increased from 9.9 to 14.3%. The plasticizer in PVA did not diffuse to the PA matrix during spinning. However, PVA could induce the crystallization of PA6 via interfacial hydrogen bonding. When the spinning speed was 1500 m/min, and PVA/PA6 was 7:3, the tensile strength reached the highest value of 1.67 cN/dtex. The uniform diameters of ultra-fine PA6 fibers (2-5 μm) were obtained by an environment-friendly water-splitting process. The "sea" phase (TPVA) in sea-island fiber could be removed quickly by boiling water treatment in 3 min. This green and energy-saving sea-island fiber splitting technique is of great significance in reducing CO