Effects of Shellac Self-Repairing and Carbonyl Iron Powder Microcapsules on the Properties of Dulux Waterborne Coatings on Wood.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 16 citations in OpenAlex.
- Preparation of UV Topcoat Microcapsules and Their Effect on the Properties of UV Topcoat Paint Film.Polymers · 2024Article
- Effect of Sandpaper Meshes on the Performance ofPolymers · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors at 1 institution in 1 country.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Magnetic carbonyl iron powder (CIP) microcapsules were created by in situ polymerization using melamine resin as the wall material and CIP as the core material. They were mixed with shellac self-repairing microcapsules to prepare dual-functional wood coatings, and the effect of different amounts of CIP microcapsules in the Dulux Waterborne primer on the performance of the primer was investigated. The findings demonstrated that the core-wall ratio had a significant impact on the characteristics of CIP microcapsules. The microcapsule coating rate reached 57.7% when the core-wall ratio was 0.65:1. The maximum reflection loss of CIP microcapsules with the core-wall ratio of 0.70:1 is -10.53 dB. When the addition amount of shellac self-repairing microcapsules is 4.2%, and the additional amount of CIP microcapsules with a core wall ratio of 0.65:1 and 0.70:1 is 3.0%, the coating color difference is the smallest. The number of microcapsules causes a noticeable drop in the coating's gloss, and the amount of microcapsules causes a small negative change in the coating's adherence. With an increase in the number of microcapsules, the coating's hardness, impact resistance, and tensile resistance first rose and subsequently fell. When the content of CIP microcapsules with core-wall ratio of 0.65:1 and 0.70:1 was 9.0%, the hardness, elongation at break and repair rate of the coating reached the best performance. According to a comprehensive analysis, when the content of CIP microcapsules with core-wall ratio of 0.70:1 is 9.0%, the coating has good performance. At this time, the coating has a color difference of 1.83, a glossiness of 19.3, an adhesion of 2 H, a hardness of 3 H, an impact resistance of 17 kg·cm, and a repair rate of 33.3%. This provides a technical basis for the application of multifunctional coatings on wooden substrates.