Study and Characterization of Regenerated Hard Foam Prepared by Polyol Hydrolysis of Waste Polyurethane.

In this paper, four different kinds of diols were used for the alcoholysis of waste thermoplastic polyurethane elastomers. The recycled polyether polyols were used to prepare regenerated thermosetting polyurethane rigid foam through one-step foaming. We used four different kinds of alcoholysis agents, according to different proportions of the complex, and we combined them with an alkali metal catalyst (KOH) to trigger the catalytic cleavage of the carbamate bonds in the waste polyurethane elastomers. The effects of the different types and different chain lengths of the alcoholysis agents on the degradation of the waste polyurethane elastomers and the preparation of regenerated polyurethane rigid foam were studied. Based on the viscosity, GPC, FT-IR, foaming time and compression strength, water absorption, TG, apparent density, and thermal conductivity of the recycled polyurethane foam, eight groups of optimal components were selected and discussed. The results showed that the viscosity of the recovered biodegradable materials was between 485 and 1200 mPa·s. The hard foam of the regenerated polyurethane was prepared using biodegradable materials instead of commercially available polyether polyols, and its compressive strength was between 0.131 and 0.176 MPa. The water absorption rate ranged from 0.7265 to 1.9923%. The apparent density of the foam was between 0.0303 and 0.0403 kg/m