Preparation and Hydration Mechanisms of Low Carbon Ferrochrome Slag-Granulated Blast Furnace Slag Composite Cementitious Materials.
Article in Materials (Basel, Switzerland), 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Durable Mortar Mixes Using 50% of Activated Volcanic Ash as A Binder.Materials (Basel, Switzerland) · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
Low carbon ferrochrome slag (LCFS) is the metallurgical waste slag from the carbon ferrochrome alloy smelting process. Compared with high carbon ferrochrome slag, LCFS has great potential as cementitious material; the chemical compositions of the two types of slag are quite different. In this research, composite cementitious materials are prepared which use low carbon ferrochrome slag and granulated blast furnace slag (GBFS) as the main raw material. Steel slag mud (SSM) and flue gas desulfurization gypsum (FGDG) are used as the activator. In order to find the variety rule of compressive strength on the composite cementitious materials, a three-factor three-level Box-Behnken design is used to discuss the following independent variables: LCFS content, GBFS content, and water-binder ratio. Moreover, the hydration characteristics of the LCFS-GBFS composite cementitious materials is studied in this paper in terms of hydration product, micromorphology, and hydration degree, based on multi-technical microstructural characterizations. The results show that the compressive strength of the LCFS-GBFS composite cementitious materials is significantly affected by single factors and the interaction of two factors. The mechanical property of the mortar samples at 3, 7, and 28 days are 26.6, 35.3, and 42.7 MPa, respectively, when the LCFS-GBFS-SSM-FGDG ratio is 3:5:1:1 and the water-binder ratio is 0.3. The hydration products of LCFS-GBFS composite cementitious materials are mainly amorphous gels (C-S-H gel), ettringite, and Ca(OH)