Is nanomaterial- and vancomycin-loaded polymer coating effective at preventing methicillin-resistant Staphylococcus aureus growth on titanium disks? An in vitro study.

purposePeriprosthetic joint infections induced by methicillin-resistant Staphylococcus aureus (MRSA) pose a major socioeconomic burden. Given the fact that MRSA carriers are at high risk for developing periprosthetic infections regardless of the administration of eradication treatment pre-operatively, the need for developing new prevention modalities is high.

methodsThe antibacterial and antibiofilm properties of vancomycin, Al

resultsAmong the tested modalities, high- and low-dose vancomycin-loaded Resomer® coating yielded the most satisfactory metalwork protection against MRSA (median absorbance was 0.1705; [IQR = 0.1745] vs control absorbance 0.42 [IQR = 0.07]; p = 0.016; biofilm reduction was 100%; and 0.209 [IQR = 0.1295] vs control 0.42 [IQR = 0.07]; p < 0.001; biofilm reduction was 84%, respectively). On the other hand, polymer coating alone did not provide clinically meaningful biofilm growth prevention (median absorbance was 0.2585 [IQR = 0.1235] vs control 0.395 [IQR = 0.218]; p < 0.001; biofilm reduction was 62%).

conclusionsWe advocate that apart from the well-established preventative measures for MRSA carriers, loading implants with bioresorbable Resomer® vancomycin-supplemented coating may decrease the incidence of early post-op surgical site infections with titanium implants. Of note, the payoff between localized toxicity and antibiofilm efficacy should be considered when loading polymers with highly concentrated antimicrobial agents.